Irradiation vulcanization of polybutadiene latex appended n-BMA and n-BA

LIU Yuguang; ZHANG Chengwu; HOU Jing; DONG Wei; ZHANG Xuequan

您当前的位置：

首页 >

文章列表页 >

Irradiation vulcanization of polybutadiene latex appended n-BMA and n-BA

更新时间：2023-03-27

- Irradiation vulcanization of polybutadiene latex appended n-BMA and n-BA
- Journal of Radiation Research and Radiation Processing Vol. 29, Issue 3, Pages: 143-148(2011)
- 作者机构：
  
  1.黑龙江省科学院技术物理研究所　哈尔滨　150086
  2.黑龙江省塑料工业研究所　哈尔滨　150001
  3.中国科学院长春应用化学研究所　长春　130022
- 作者简介：
- 基金信息：
- DOI：
  CLC：
扫描看全文
LIU Yuguang, ZHANG Chengwu, HOU Jing, et al. Irradiation vulcanization of polybutadiene latex appended n-BMA and n-BA. [J]. Journal of Radiation Research and Radiation Processing 29(3):143-148(2011)
DOI：

LIU Yuguang, ZHANG Chengwu, HOU Jing, et al. Irradiation vulcanization of polybutadiene latex appended n-BMA and n-BA. [J]. Journal of Radiation Research and Radiation Processing 29(3):143-148(2011) DOI：

摘要

在,60,Co γ射线辐照下，以甲基丙烯酸丁酯（n-BMA）和丙烯酸丁酯（n-BA）作为敏化剂对聚丁二烯胶乳（PBL）进行辐射硫化，探讨敏化辐射交联机理和交联行为。研究了敏化剂和吸收剂量对聚丁二烯橡胶的交联、力学性能及动态力学性能的影响，并采用红外吸收光谱对辐照交联产物分子结构予以表征。结果表明，随交联密度增加，玻璃化转变温度（,T,g,）升高，室温弹性模量（,E,’）和损耗模量（,E,”）增大，抗张强度和杨氏模量增大，但断裂伸长率降低。提示n-BMA和n-BA均对聚丁二烯胶乳具有交联敏化作用，且偏离Charlesby-Pinner关系式，不符合无规交联规律。

Abstract

Irradiation vulcanization of polybutadiene rubber latex (PBL) in the presence of radiation sensitizer n-butyl methacrylate (n-BMA) and n-butyl acrylate (n-BA) by ,60,Co γ-rays was studied. The crosslinking mechanism and kinetics of irradiation vulcanization were investigated. The effect of absorbed doses and the sensitizer contents on the gel fraction was evaluated, and the micro structure, mechanical and dynamic mechanical properties of latex films were characterized by means of FTIR and DMA, etc. The results indicated that both of n-BMA and n-BA showed vulcanization enhancement for PBL. With increment of crosslink density, the tensile strength and Young’s modulus increased while elongation at break decreased. Moreover, as heavy crosslinking restrained the movement of chains the glass transition temperature (,T,g,) increased, and the storage modulus (,E,’) and loss modulus (,E,") at room temperature increased as well. The deviation from the Charlesby-Pinner equation revealed PBL enhancement vulcanization, which didn’t fit well with kinetic randomly.

关键词

辐射交联聚丁二烯胶乳敏化剂凝胶分数

Keywords

Irradiation vulcanizationPolybutadiene latexSensitizerGel fraction

references

Views

下载量

CSCD

Alert me when the article has been cited

提交

Tools

Publicity Resources

Irradiation and sensitizing effects on chitosan degradation

Research and application of fuzzy subtractive clustering model on tensile strength of radiation vulcanization for nitrile -butadiene rubber

Vulcanization of polybutadiene latex induced by ⁶⁰Co γ-rays irradiation

SYNTHESIS OF SiC CERAMICS BY PYROLYSIS OF ELECTRON BEAM IRRADIATED POLYCARBOSILANEⅡ.SENSITIZING EFFECT OF LOW MOLECULAR WEIGHT POLYBUTADIENE ON CURING REACTION

STUDY ON THE KINETICS OF GEL FORMATION IN THE RADIATION CROSSLINKING REACTION

Related Author

No data

Related Institution

Zhejiang Institute of Application Energy and Nuclear Technology

Zhejiang University

School of Textile and Clothing Engineering of Soochow University

Institute of Electrical and Mechanical Services Suchow University

Institute of Radiation Technique Soochow University

⁰