HDPE/EPDM/硅橡胶/CB的PTC材料（挤出成型）辐照前后的特性研究

贾少晋; 徐忠庭; 张志成; 江平开; 修其辉; 王宗光

您当前的位置：

首页 >

文章列表页 >

HDPE/EPDM/硅橡胶/CB的PTC材料（挤出成型）辐照前后的特性研究

研究论文 | 更新时间：2023-03-30

- HDPE/EPDM/硅橡胶/CB的PTC材料（挤出成型）辐照前后的特性研究
- Studies on the effects of EPDM, SR on PTC- of HDPE/CB before and after γ-radiation
- 辐射研究与辐射工艺学报 2004年22卷第6期页码：329-333
- 作者机构：
  
  1.上海交通大学化学化工学院高分子科学与工程系　上海　200240
  2.芜湖佳宏新材料有限公司　芜湖　241000
  3.中国科学技术大学高分子科学与工程系　合肥　230026
- 作者简介：
  
  贾少晋，男，1968年10出生，2002年在中国科学技术大学获博士学位，高分子辐射化学专业
- 基金信息：
- DOI：
  中图分类号：
扫描看全文
贾少晋, 徐忠庭, 张志成, 等. HDPE/EPDM/硅橡胶/CB的PTC材料（挤出成型）辐照前后的特性研究[J]. 辐射研究与辐射工艺学报, 2004,22(6):329-333.

JIA Shaojin, XU Zhongting, ZHANG Zhicheng, et al. Studies on the effects of EPDM, SR on PTC- of HDPE/CB before and after γ-radiation[J]. Journal of Radiation Research and Radiation Processing, 2004,22(6):329-333.
贾少晋, 徐忠庭, 张志成, 等. HDPE/EPDM/硅橡胶/CB的PTC材料（挤出成型）辐照前后的特性研究[J]. 辐射研究与辐射工艺学报, 2004,22(6):329-333. DOI：

JIA Shaojin, XU Zhongting, ZHANG Zhicheng, et al. Studies on the effects of EPDM, SR on PTC- of HDPE/CB before and after γ-radiation[J]. Journal of Radiation Research and Radiation Processing, 2004,22(6):329-333. DOI：

摘要

对掺杂了导电碳黑（CB）的高密度聚乙烯（HDPE）/三元乙丙橡胶（EPDM）和HDPE/EPDM/Si rubber（硅橡胶）的挤出样品进行了辐照前后的电性能表征。研究了正温度系数（PTC）功能材料挤出后的特性，发现挤出后粒子和聚合物取向对材料电性能都有较大影响。经γ射线辐照后HDPE/EPDM/Si rubber/CB功能复合材料稳定性大为提高，初步探讨了辐射对PTC功能材料稳定性的影响。加入硅橡胶，可增强CB粒子与基体的亲和力，增加粒子的分散性，提高电阻的长期稳定性，并使工作温度得以长期保持。

Abstract

High-density-polyethylene (HDPE), Si rubber (SR) and ethylene-density-polyethylene (EPDM) were used as the polymer matrices, A kinds of carbon blacks was used as the conductive filler. The positive temperature coefficient (PTC) intensity of the HDPE/CB, HDPE/EPDM /CB composites flow during extrusion to produced was tested before and after irradiation. Compared to that of HDPE/CB composites, the electrical reproducibility of the irradiated HDPE/EPDM /CB composites of is better. The effects of γ-rays irradiation were also estimated. The results showed that the reproductive of the PTC effect was related to the adhesion between the interface of the polymer matrices and CB particles. These PTC phenomena and their distinctive aspects were described. The explanations were given from the structural characteristics of the blends, CB particles distribution and motion of polymer segments.

关键词

高密度聚乙烯负温度系数正温度系数硅橡胶炭黑

Keywords

High-density-polyethylene (HDPE)Negative temperature coefficient (NTC)Positive temperature coefficient (PTC) intensitySi RubberCarbon black

references

浏览量

下载量

CSCD

文章被引用时，请邮件提醒。

提交

工具集

关联资源

低浓度CB 填充的HDPE复合体系的流变学性质及其辐照响应

辐射制备POE/EPDM/SR/MH无卤阻燃绝缘材料的研究

辐射交联对聚合物/炭黑导电复合物影响的评述

辐射交联对LDPE/CB复合物PTC效应稳定性的影响

γ辐照制备耐高温阻燃电缆材料的研究^*