- γ共辐射接枝丙烯酸改善聚醚砜粉体亲水性的研究
- Hydrophilicity improvement of polyethersulfone powders by grafting acrylic acid with γ−ray simultaneous irradiation method
- 辐射研究与辐射工艺学报 2005年23卷第6期页码：337-341
- 作者机构：
  
  1.中国科学院上海应用物理研究所　上海　201800
- 作者简介：
  
  邓波，男，1978年4月出生，2000年毕业于华东理工大学化学系。现为上海应用物理研究所无机化学专业博士研究生
  侯铮迟
- 基金信息：
- DOI：
  中图分类号：
扫描看全文
邓波, 侯铮迟, 张凤英, 等. γ共辐射接枝丙烯酸改善聚醚砜粉体亲水性的研究[J]. 辐射研究与辐射工艺学报, 2005,23(6):337-341.

DENG Bo, HOU Zhengchi, ZHANG Fengying, et al. Hydrophilicity improvement of polyethersulfone powders by grafting acrylic acid with γ−ray simultaneous irradiation method[J]. Journal of Radiation Research and Radiation Processing, 2005,23(6):337-341.
邓波, 侯铮迟, 张凤英, 等. γ共辐射接枝丙烯酸改善聚醚砜粉体亲水性的研究[J]. 辐射研究与辐射工艺学报, 2005,23(6):337-341. DOI：

DENG Bo, HOU Zhengchi, ZHANG Fengying, et al. Hydrophilicity improvement of polyethersulfone powders by grafting acrylic acid with γ−ray simultaneous irradiation method[J]. Journal of Radiation Research and Radiation Processing, 2005,23(6):337-341. DOI：

摘要

利用γ射线共照射技术在聚醚砜（Polyethersulfone，PES）粉体上接枝了丙烯酸。研究了丙烯酸单体体积分数、接枝溶液pH值、吸收剂量、阻聚剂（Cu,2+,）浓度等对接枝率的影响规律。通过与称重法相结合，得到了利用红外光谱对接枝率进行定量分析的工作曲线。研究结果表明，当吸收剂量为25kGy、单体体积分数为30%、阻聚剂用量为0.004mol/L时，可以获得最高的接枝率。接枝溶液中盐酸的添加有利于提高接枝率。提高接枝率有助于改善PES的亲水性。

Abstract

Acrylic acid was grafted to Polyethersulfone (PES) powders by liquid−phase simultaneous irradiation. Effects of grafting conditions, such as absorbed dose, Volume fraction of monomer, inhibitor (Cu,2+,) concentration, and pH of the grafting solution on degree of the grafting were investigated. Combined with gravimetric analysis, a working curve of grafting degree through FT−IR quantitative analysis was obtained. The highest grafting degree was achieved at dose of 25kGy, Volume fraction of monomer of 30% and inhibitor concentration of 0.004 mol/L. Greater degrees of the grafting could be obtained by adding increasing amount of hydrochloric acid to the system. Hydrophilicity of the grafted PES powders increased with higher degrees of the grafting.

关键词

辐射接枝亲水性聚醚砜丙烯酸阻聚剂

Keywords

Radiation graftingHydrophilicityPolyethersulfone (PES)Acrylic acidInhibitor

references

浏览量

下载量

CSCD

文章被引用时，请邮件提醒。

提交

工具集

关联资源

两种共聚单体对淀粉/聚丙烯酸钠超级吸水材料耐盐性能的影响

辐射法制备淀粉基超级吸水材料及其性能

辐照接枝改性涤纶织物的亲水性能

接枝丙烯酸聚乙烯表面诱导生成硫化镉及其形貌研究

γ辐射接枝甲基丙烯酸改善聚醚砜膜亲水性的研究