Characteristic study of pre-irradiated HDPE grafted with NIPA/AAc

更新时间：2023-03-30

- Characteristic study of pre-irradiated HDPE grafted with NIPA/AAc
- Journal of Radiation Research and Radiation Processing Vol. 22, Issue 5, Pages: 271-275(2004)
- 作者机构：
  
  1.上海大学射线应用研究所　上海　201800
- 作者简介：
- 基金信息：
- DOI：
  CLC：
扫描看全文
LIU Zhaomin, XIAO Hui, FU Qun, et al. Characteristic study of pre-irradiated HDPE grafted with NIPA/AAc. [J]. Journal of Radiation Research and Radiation Processing 22(5):271-275(2004)
DOI：

LIU Zhaomin, XIAO Hui, FU Qun, et al. Characteristic study of pre-irradiated HDPE grafted with NIPA/AAc. [J]. Journal of Radiation Research and Radiation Processing 22(5):271-275(2004) DOI：

摘要

高密度聚乙烯膜（HDPE）在N,2,保护下预辐射接枝N-异丙基丙烯酰胺（NIPA）和丙烯酸（AAc），制备了既具有温度敏感又兼具pH敏感的水凝胶，应用傅立叶变换红外光谱（FTIR）、差示扫描量热仪（DSC）、扫描电镜（SEM），研究了该水凝胶的接枝物组成、物理性质以及表面形态。结果表明接枝复合物在不同pH值的介质环境中表现出不同的温敏特性：在酸性条件下随温度升高，体积溶胀增加，表现为“热胀温敏水凝胶”；在中性或碱性条件下随温度升高，溶胀体积在相变温度附近急剧收缩，表现为“热缩温敏水凝胶”。

Abstract

HDPE preirradiated under nitrogen protection was grafted with NIPA/AAc. The grafted hydrogel is temperature and pH sensitive. FTIR, DSC, SEM were used to study the composition, properties and surface morphology of the hydrogel. Results showing that LCST characteristics was different under different pH environment. Under acid condition, hydrogel volume increased with increasing temperature, indicating the hydrogel being heat expansive and temperature sensitive. Under neutral or alkaline condition, hydrogel volume contracted rapidly near phase transition with increasing temperature, indicating the hydrogel being heat shrinking and temperature sensitive.

关键词

预辐射接枝环境敏感水凝胶

Keywords

Preirradiation graftingEnvironmental sensitivenessHydrogel

references

Views

下载量

CSCD

Alert me when the article has been cited

提交

Tools

Publicity Resources

Preparation of environmentally sensitive hydrogel by preirradiation graftingof NIPA/AAc onto HDPE membrane

Preparation of hydrogel-based photocatalytic composite materials by radiation technology

Radiation preparation and application status of photosensitive antibacterial composite hydrogel

Radiation preparation and mechanical properties of a high-strength graphene oxide/ highly substituted hydroxypropyl cellulose/polyvinyl alcohol composite hydrogel

Preparation of hydrogel containing Angelica dahurica coumarin by radiation crosslinking and its properties

Related Author

No data

Related Institution

Applied Radiation Institute, Shanghai University

Xianning High-tech Hydrogel Dressing Industry Technology Research Institute

College of Pharmacy, Hubei University of Science and Technology

Hubei Key Laboratory of Radiation Chemistry and Functional Materials, Hubei University of Science and Technology

School of Chemistry and Chemical Engineering, Wuhan University of Science and Technology

⁰