INFLUENCE OF γ RAY IRRADIATION ON THE STRUCTURE AND PROPERTIES OF FLUORORUBBER F2311

LUO Shikai; FU Yibei; LUO Shunhuo; LONG Xinping; HUANG Yigan

您当前的位置：

首页 >

文章列表页 >

INFLUENCE OF γ RAY IRRADIATION ON THE STRUCTURE AND PROPERTIES OF FLUORORUBBER F2311

更新时间：2023-04-07

- INFLUENCE OF γ RAY IRRADIATION ON THE STRUCTURE AND PROPERTIES OF FLUORORUBBER F2311
- Journal of Radiation Research and Radiation Processing Vol. 20, Issue 1, Pages: 12-18(2002)
- 作者机构：
  
  1.中国工程物理研究院化工材料研究所　绵阳　621900
  2.中国工程物理研究院　绵阳　621900
- 作者简介：
- 基金信息：
- DOI：
  CLC：
扫描看全文
LUO Shikai, FU Yibei, LUO Shunhuo, et al. INFLUENCE OF γ RAY IRRADIATION ON THE STRUCTURE AND PROPERTIES OF FLUORORUBBER F2311. [J]. Journal of Radiation Research and Radiation Processing 20(1):12-18(2002)
DOI：

LUO Shikai, FU Yibei, LUO Shunhuo, et al. INFLUENCE OF γ RAY IRRADIATION ON THE STRUCTURE AND PROPERTIES OF FLUORORUBBER F2311. [J]. Journal of Radiation Research and Radiation Processing 20(1):12-18(2002) DOI：

摘要

氟橡胶F2311在真空、氮气、空气3种气氛经50—1000kGy的γ射线辐照后其平均分子量、抗拉强度、断裂伸长率都随剂量的增大而降低，凝胶含量随剂量的增大先降低而后升高，750kGy时达到最低点，其玻璃化温度、贮存模量与凝胶含量变化相同。样品的IR分析表明产生了—CF=CH—、—CF=CF—、—C=O等基团。用SEM观测了辐照后样品的微观形貌。研究表明，空气气氛将促进F2311的辐射降解，氮气气氛有一定的抑制作用。

Abstract

After irradiation of F2311 by γ ray (50—1000kGy) in vacuum, nitrogen and air, its average molecular weight, tensile strength and breaking elongation decreased as irradiation dose increased. But the gel fraction at first decreased and then increased with the increment of dose, on the dose of 750kGy the minimum value has been obtained. The changes of glass transition temperature and modulus are similar to that of the gel fraction. The IR analysis of sample indicated the formation of — CF=CH —, — FC=CF — and — C=O groups. Microstructures for irradiated samples were studied by SEM. Results showed that air promoted the irradiation degradation of F2311 and nitrogen inhibited that of it in a certain extent.

关键词

氟橡胶F2311γ射线辐射降解

Keywords

Fluororubber F2311γ rayRadiation degradation

references

Views

下载量

CSCD

Alert me when the article has been cited

提交

Tools

Publicity Resources

STUDY ON GAS PRODUCTS OF FLUORORUBBER F2311 AFTER RADIATION DEGRADATION

Studies on γ-irradiation-induced-degradation of chloramphenicol in aqueous solution

Recent advances on radiation degradation of polysulfone

γ-ray degradation of chitosan to prepare water-soluble oligomers

The γ-irradiation stability of anhydrous ethylenediamine

Related Author

No data

Related Institution

Material Institute of Chemistry and Engineering,CAEP

Institute of Nuclear Physics and Chemistry, CAEP

Institute of Agro food Science and Technology, Chinese Academy of Agricultural Sciences, The Key Open Laboratory of Agricultural Nuclear Technology and Processing of Agro-food of Ministry of Agriculture

Institute of Machinery Manufacturing Technology, China Academy of Engineering Physics

Department of Medical Physics, College of Material Science and Technology, Nanjing University of Aeronautics and Astronautics

⁰