EFFECTS OF γ-IRRADIATION AND THERMAL TREATMENT ON CRYSTALLINITY OF DRAWN HDPE

Liu Zhanjun; Joseph Silverman

您当前的位置：

首页 >

文章列表页 >

EFFECTS OF γ-IRRADIATION AND THERMAL TREATMENT ON CRYSTALLINITY OF DRAWN HDPE

更新时间：2023-04-23

- EFFECTS OF γ-IRRADIATION AND THERMAL TREATMENT ON CRYSTALLINITY OF DRAWN HDPE
- Journal of Radiation Research and Radiation Processing Vol. 15, Issue 2, Pages: 91-95(1997)
- 作者机构：
  
  1.中国科学技术大学应用化学系　合肥　230026
  2.Department of Materials and Nuclear Engineering,University of Maryland, USA
- 作者简介：
- 基金信息：
- DOI：
  CLC：
扫描看全文
Liu Zhanjun, Joseph Silverman. EFFECTS OF γ-IRRADIATION AND THERMAL TREATMENT ON CRYSTALLINITY OF DRAWN HDPE. [J]. Journal of Radiation Research and Radiation Processing 15(2):91-95(1997)
DOI：

Liu Zhanjun, Joseph Silverman. EFFECTS OF γ-IRRADIATION AND THERMAL TREATMENT ON CRYSTALLINITY OF DRAWN HDPE. [J]. Journal of Radiation Research and Radiation Processing 15(2):91-95(1997) DOI：

摘要

研究了在真空和空气中γ辐照对拉伸高密度聚乙烯（HDPE）结晶度的影响。结果表明：真空中辐照约250kGy吸收剂量，拉伸HDPE的结晶度随吸收剂量的增加而降低，然后吸收剂量的增加对其结晶度基本上无影响；而在空气中辐照至1000kGy的吸收剂量，拉伸HDPE的结晶度基本保持不变。同时还研究了不同温度热处理对未辐照拉伸HDPE的结晶度影响，其结晶度首先随热处理温度的增加而迅速增加，约120 ℃时达到极大值。而后随热处理温度的进一步增加而迅速下降。由拉伸HDPE中存在大量空隙及结晶缺陷和聚乙烯的辐射化学反应解释了上述实验结果。

Abstract

The effect of absorbed dose irradiated in vacuum and air on the crystallinity of drawn HDPE was studied. Experimental results show that up to 250kGy of absorbed dose when irradiated in vacuum,the crystallinity of drawn HDPE is decreased from about 75% to about 71%,and then the increase of absorbed dose until 1000kGy has no further effect in lowering thecrystallinity; when irradiated in air,an absorbed dose of 1000kGy has noeffect on the crystallinity of drawn HDPE. The effect of temperature of thermal treatment on the crystallinity of unirradiated drawn HDPE was alsoinvestigated. At first,the crystallinity is increased with the increase oftemperature of thermal treatment, at about 120℃,it reaches the maximumvalue, and then it is repidly lowered with the further increase of temperatureof thermal treatment. Based on the existence of a lot of voids and latticedefects inside the drawn HDPE,the above experimental results were explained.

关键词

γ辐照高密度聚乙烯拉伸热处理结晶度

Keywords

γ-irradiationHigh density polyethyleneDrawnThermal treatmentCrystallinity

references

Views

下载量

CSCD

Alert me when the article has been cited

提交

Tools

Publicity Resources

Supercritical carbon dioxide foaming behavior and properties of radiation cross-linked polypropylene random copolymer

Decontamination of tritium from irradiated nuclear graphite

Study on the ⁶⁰Co γ-irradiation stability of fullerenes

Effect on molecular weight of poly (L-lactic acid) by irradiation graft with NVP

Study on anti-radiation character of GMR multi-films

Related Author

No data

Related Institution

Zhejiang Sinco-polymer Material R&D Centre, Jiashan

Shanghai Institute of Applied Physics, Chinese Academy of Sciences

School of Chemical Engineering, Xiangtan University

University of Chinese Academy of Sciences

Institute of Nuclear Physics and Chemistry, China Academy of Engineering Physics

⁰