A study on the oxidation of high density polyethylene (HDPE) by γ ray irradiation in oxygen atmosphere has been made. The influence of irradiated time on the oxidation has been investigated with the help of Fourier Transform Infrared– Photoacoustics Spectroscopy (FTIR-PAS) . Results of FTIR-PAS show after irradiation groups like -C=O, -O-C-O-, O=C-O- were introduced into the HDPE. Although the γ ray has powerful penetrability, the oxidation mainly takes place on the surface of HDPE. After 4h irradiation in oxygen (dose rate 66Gy/min. ) , -C=O is the main group which was introduced into the surface of HDPE. Lengthening the irradiation process makes the pre-produced oxidized section in HDPE surface continue their reactions to yield some oxidation products with the structures of -O-C-O-, O=C-O- and so on. FTIR shows there are reactions or week interaction like hydrogen bond between the irradiated HDPE and PA6 in the binary blends, this is helpful to increase the compatibility of the phase of HDPE and polyamide-6(PA6) in the blend. Scanning Electron Microscope (SEM) result shows that the interface between HDPE matrix and PA6 domains is much clear and smoother in 0γHDPE/PA6 blends than in 4γHDPE/PA6 and 7γHDPE/PA6 blends. These suggested the miscibility of PA6 and HDPE was improved after HDPE irradiating in oxygen by γ ray radiation.