辐射交联聚氯乙烯绝缘材料的研究Ⅱ.添加一缩二乙二醇二丙烯酸酯的影响

周积春; 朱振康; 施松远; 冯幼芳; 刘钰铭; 赵以正; 任惠芳; 陈先为; 赵杰; 陈建聪; 印秀凤

您当前的位置：

首页 >

文章列表页 >

辐射交联聚氯乙烯绝缘材料的研究Ⅱ.添加一缩二乙二醇二丙烯酸酯的影响

更新时间：2023-04-23

- 辐射交联聚氯乙烯绝缘材料的研究Ⅱ.添加一缩二乙二醇二丙烯酸酯的影响
- STUDY ON RADIATION CROSSLINKING OF PVC INSULATION MATERIALS PART Ⅱ DGDA EFFECT
- 辐射研究与辐射工艺学报 1989年7卷第1期页码：45-50
- 作者机构：
  
  1.上海科学技术大学，上海
  2.上海化工厂，上海
- 作者简介：
- 基金信息：
- DOI：
  中图分类号：
扫描看全文
周积春, 朱振康, 施松远, 等. 辐射交联聚氯乙烯绝缘材料的研究Ⅱ.添加一缩二乙二醇二丙烯酸酯的影响[J]. 辐射研究与辐射工艺学报, 1989,7(1):45-50.

Zhou Jichun, Zhu Zhenkang, Shi Songyuan, et al. STUDY ON RADIATION CROSSLINKING OF PVC INSULATION MATERIALS PART Ⅱ DGDA EFFECT[J]. Journal of Radiation Research and Radiation Processing, 1989,7(1):45-50.
周积春, 朱振康, 施松远, 等. 辐射交联聚氯乙烯绝缘材料的研究Ⅱ.添加一缩二乙二醇二丙烯酸酯的影响[J]. 辐射研究与辐射工艺学报, 1989,7(1):45-50. DOI：

Zhou Jichun, Zhu Zhenkang, Shi Songyuan, et al. STUDY ON RADIATION CROSSLINKING OF PVC INSULATION MATERIALS PART Ⅱ DGDA EFFECT[J]. Journal of Radiation Research and Radiation Processing, 1989,7(1):45-50. DOI：

摘要

本文研究了聚氯乙烯（PVC）在添加一缩二乙二醇二丙烯酸酯双官能团单体（DGDA）条件下的辐射交联效应。辐射初期PVC的交联反应速度较快，当剂量达到40 kGy以后，凝胶含量达到最大值。在相同剂量条件下，PVC的凝胶含量、交联G值随DGDA添加量的增加而提高。,交联PVC比未交联PVC的体积电阻系数有明显的提高，说明PVC辐射交联后的电绝缘性能得到很大改善。交联后，它的机械性能也有一定的提高。,辐射交联PVC的热老化失重比未交联的PVC有较大的减少，而拉伸强度残留率K,1,和断裂伸长率残留率K,2,比未交联的PVC有较大提高，也就是说PVC交联后的耐温性提高了。

Abstract

This paper reports the effect of difunctional monomer, diethylene glycol diacrylate (DGDA) on radiation crosslinking of PVC.,Crosslinking of PVC proceeds very rapidly during the initial period of irradiation. When the dose reaches 40 kGy, it slows down and the gel content tends to level off. Under the same dose condition, PVC gel content and G value increase with increase of the amount of DGDA.,Radiation Crosslinked PVC has a good insulating property and mechanical property.,By comparing crosslinked PVC with uncrosslinked PVC, the loss weight after thermal aging of crosslinked PVC has a great decrease. But the tensile strength after aging (K,1,) and the elongation after aging (K,2,) of crosslinked PVC have a great increase respectively. It was also found that the heat-resisting property of PVC had been improved after being crosslinked.

关键词

辐射引发辐射交联聚氯乙烯一缩二乙二醇二丙烯酸酯凝胶含量

Keywords

RadiationRadiation CrosslinkingPolyvinyl chloride (PVC)Diethylene glycol diacrylate (DGDA)Gel content

references

浏览量

下载量

CSCD

文章被引用时，请邮件提醒。

提交

工具集

关联资源

辐射法制备聚乙烯醇（PVA）改性的聚对苯二甲酸乙二醇酯（PET）薄膜及其防雾性能

吸收剂量对二聚酸型聚酰胺结构及性能的影响

高强度氧化石墨烯/高取代羟丙基纤维素/聚乙烯醇复合水凝胶的辐射制备及其机械性能

交联固化对碳化硅纤维耐热性能的影响

辐照乙烯-四氟乙烯共聚物的热老化性能